Batı, SerkanKılıç, MusaKırık, İhsan2021-11-262021-11-262017-01Batı, S., Kılıç, M., Kırık, İ. (2017). Production of Intermetallic FGM. Middle East Journal of Technic (MEJT), 2 (1), pp.119-135.2536-5304https://hdl.handle.net/20.500.12402/4092NiAl and NiTi intermetallic materials are among advanced technology materials that have outstanding mechanical and physical properties for high temperature applications. Particularly, creep resistance, low density and high hardness properties stand out in such intermetallics. It is known that Ni-Al intermetallics are commonly used in various application fields with the addition of Ti for improving properties there of (in terms of low density, high hardness and shear strength) in the produced intermetallics. In this study, with different features -325 mesh Al, Ni and Ti powders are mixed to form NiTi, Ni3Al and NiAl in atomic ratio. Sintering process was used in this study by adding different amounts of powder mixture. The mixed powders were pressed at a pressure of 100 MPa in a metal die at room temperature. Three important intermetallic compounds were produced by SHS method, by using different process parameters to obtain functionally-graded materials having different features of NiAl, Ni3Al and NiTi alloys. Analyses were conducted metallographically on the samples after producing, face propagation were calculated and hardness were determinedeninfo:eu-repo/semantics/openAccessAttribution-NonCommercial-ShareAlike 3.0 United StatesNiAl and NiTi Intermetallic MaterialsSelf-Propagating High Temperature SynthesisFunctionally-Graded MaterialArticle21119135