NiAl and NiTi intermetallic materials are among advanced technology materials that have
outstanding mechanical and physical properties for high temperature applications. Particularly, creep resistance,
low density and high hardness properties stand out in such intermetallics. It is known that Ni-Al intermetallics
are commonly used in various application fields with the addition of Ti for improving properties there of (in
terms of low density, high hardness and shear strength) in the produced intermetallics. In this study, with
different features -325 mesh Al, Ni and Ti powders are mixed to form NiTi, Ni3Al and NiAl in atomic ratio.
Sintering process was used in this study by adding different amounts of powder mixture. The mixed powders
were pressed at a pressure of 100 MPa in a metal die at room temperature. Three important intermetallic
compounds were produced by SHS method, by using different process parameters to obtain functionally-graded
materials having different features of NiAl, Ni3Al and NiTi alloys. Analyses were conducted metallographically
on the samples after producing, face propagation were calculated and hardness were determined
Açıklama
Anahtar Kelimeler
NiAl and NiTi İntermetallic Materials, Self-Propagating High Temperature Synthesis, Functionallygraded Material