The influence of adherend width on tensile strength and failure load of Z joints bonded with adhesive

In this study, the influence of the adherend width on the tensile strength and failure loads of Z joints were analyzed both experimentally and numerically. The Z joints were subjected to tensile load in the experiments. The stress analyses were executed using the finite element method (FEM). The FEM analyses were performed with Ansys (v.14.0.1). The FEM analyses were carried out to investigate the stress and strain distributions in the adhesive layer of the Z joints. Experimental results were also compared with numerical results, thus they were found quite reasonable. The results showed that the joint strength and failure loads increased when specimen width (b) was increased. Lowest failure load was also determined at the 10 mm width for each specimen. In order to increase the performance of the joint, 30 mm was found to be the most suitable value of width

Bu çalışmada, yapıştırma genişliğinin Z bağlantılarının çekme mukavemeti ve kırılma yüklerine etkisi deneysel ve sayısal olarak analiz edilmiştir. Z mafsalları çekme yüküne maruz kalmıştır. deneyler. Gerilme analizleri, sonlu elemanlar yöntemi (FEM) kullanılarak gerçekleştirilmiştir. FEM analizler Ansys (v.14.0.1) ile yapılmıştır. araştırmak için FEM analizleri yapılmıştır. Z bağlantılarının yapışkan tabakasındaki gerilim ve gerinim dağılımları. Deneysel sonuçlar da sayısal sonuçlarla karşılaştırıldığında oldukça makul bulunmuştur. Sonuçlar gösterdi ki, numune genişliği (b) arttığında eklem mukavemeti ve kırılma yükleri artmıştır. En düşük arıza yükü ayrıca her numune için 10 mm genişlikte belirlenmiştir. Performansını artırmak için, derz, 30 mm en uygun genişlik değeri olarak bulunmuştur.