    A research on the fatigue strength of the single-lap joint joints bonded with nanoparticle-reinforced adhesive
    (Welding in the World, 2021-01) Adin, Hamit; Saraç, İsmail; Temiz, Şemsettin
    Nano-technological developments, which have made significant progress in recent years, have significant impact on the science of adhesives. Therefore, in our study, the static and fatigue strengths of single-lap joints (SLJs) incorporating nanoparticles were compared to those without nanoparticles. Steel plates were used in the adhesive joints. The results revealed that average damage load increased significantly in nanoparticle-reinforced adhesive joints. The highest damage load was obtained with 4 wt% nanoAl2O3 in epoxy adhesive. As the average damage load increased, the locus of damage changed from interfacial to the mixture of interfacial and cohesive. Also, fatigue strengths of the joints increased when the adhesive joint had nano-Al2O3 and nano-SiO2, and decreased when the adhesive joint had nano-TiO2.
  • Küçük Resim Yok
    Öğe
  • Küçük Resim
    Öğe
    Investigation of the effect of use of Nano-Al2O3, Nano-TiO2 and Nano-SiO2 powders on strength of single lap joints bonded with epoxy adhesive
    (Elsevier, 2019-06) Adin, Hamit; Temiz, Şemsettin; Saraç, İsmail
    In this study, single lap joints were formed by adding nano-Al2O3, nano-TiO2and nano-Al2O3powders in variousproportions to the epoxy adhesive and using the additive-free epoxy adhesive; and also the mechanical prop-erties of the connections were experimentally investigated at 20, 25, 30, 50 and 70 mm overlap lengths undershear load. In the experimental work, DP460 epoxy adhesive was used as adhesive and AISI 304 stainless steelplate as adherent material. When the results obtained from the experiments were examined, it was revealed thatthe average damage load in connection with the use of nanoparticle-added adhesives increased considerably ingeneral. As a result of the experiments, the most effective nanoparticle in increasing the failure strength of theadhesive joints with nano-Al2O3particles and the maximum failure strength increase rate was 20 mm in overlaplength and 97% in 4 wt% nano-Al2O3reinforced specimens. It was also found that the nanoparticle strain was animportant parameter in the tensile strength of the adhesive joints. In addition, it has been found that the additionof nanoparticles into the adhesive increases the elongation of the joints. When the adhesion surfaces of thesamples were examined as in the case of plain adhesives, damage was observed as adhesion separation whilenanoparticle reinforcement was observed as a mixture of adhesion and cohesion.
  • Küçük Resim
    Öğe
    Tek tesirli yapıştırma bağlantılarında epoksi yapıştırıcı içerisinde nanopartikül kullanılmasının bağlantının statik ve yorulma mukavemetine etkisinin araştırılması
    (Batman Üniversitesi Fen Bilimleri Enstitüsü, 2018-02-02) Saraç, İsmail; Temiz, Şemsettin
    Yapıştırma bağlantılarında, yapıştırıcı içerisine katılan nanopartiküllerin, bağlantıların mekanik özelliklerine etkisi ile ilgili araştırmalar son zamanlarda dikkat çekmektedir. Bu çalışmada; epoksi yapıştırıcı içerisine farklı oranlarda Al2O3, TiO2 ve SiO2 nanopartikülleri katılarak ve katkısız epoksi yapıştırıcı kullanılarak tek tesirli bindirme bağlantıları oluşturulmuş ve bağlantıların statik ve yorulma dayanımları 20, 25 ve 30 mm bindirme boylarında deneysel olarak incelenmiştir. Deneysel çalışmalarda yapıştırıcı olarak DP460 epoksi yapıştırıcı ve yapıştırılan malzeme olarak AISI 304 paslanmaz çelik plaka kullanılmıştır. Deneylerden elde edilen sonuçlar incelendiğinde; nanopartikül katkılı yapıştırıcıların kullanılmasıyla elde edilen bağlantılarda genel olarak ortalama hasar yükü dikkate değer şekilde artmıştır. Yapılan deneyler sonucunda, en büyük ortalama hasar yükü, %4-Al2O3 takviyeli numunelerde elde edilmiştir. Statik testler sonucunda numunelerin yapışma yüzeyleri incelendiğinde katkısız yapıştırıcı kullanılan numunelerde hasar adhezyon ayrılması şeklinde gözlemlenirken, nanopartikül takviyesiyle hasar adhezyon ve kohezyon karışımı şeklinde gözlemlenmiştir. Yorulma deneyleride frekans 10 Hz, yükleme oranı ( R ) ise 0.1 olarak sabit alınmıştır. Yorulma deneyleri sonucunda Al2O3 ve SiO2 katkılı numunelerde bağlantıların yorulma dayanımı artarken TiO2 katkılı numunerlerde yorulma dayanımı azalmıştır.