28 sonuçlar
Arama Sonuçları
Listeleniyor 1 - 10 / 28
Öğe Effect of tightening torque on the fatigue strength of bolted composite lap joints(Kilis 7 Aralık Üniversitesi, 2016) Topkaya, Tolga; Solmaz, Murat YavuzÖğe Investigation of low velocity impact behaviors of honeycomb sandwich composites(SpringerLink, 2018-08-09) Topkaya, Tolga; Solmaz, Murat YavuzHoneycomb sandwich composites are used as significant structural members in advanced engineering applications. Thus, it is critical to determine how they behave under impact loading, in addition to other loads. In this study, low velocity impact loading behaviors of honeycomb sandwich composites were experimentally investigated. Almost all of the design parameters of honeycomb sandwich composites were investigated. The results indicated that the core thickness of honeycomb had no effect on the strength of the composite, and the parameter influencing the impact behavior of the specimen the most was the face sheet thickness. When the face sheet thickness of the specimen was increased, the most apparent strength increase was observed in the models using carbon fiber-reinforced composite face sheets. For all face sheet types subject to impact energy of 10 Joules, the upper face sheets of 0.5 mm-thick specimens were perforatedÖğe Bal peteği sandviç kompozitlerin düşük hızlı darbe testi sonrası eğilme mukavemetindeki değişimin araştırılması(Yunus Emre Enstitüsü, 2017) Topkaya, Tolga; Solmaz, Murat YavuzTeknolojinin farklı endüstri alanlarında gelişmesi ile birlikte enerji sönümleme ve hafif şok emicilerine olan ihtiyacın artması bal peteği sandviç kompozitler gibi yapılara olan ilgiyi arttırmıştır. Gerçekleştirilen çalışmada bal peteği sandviç kompozitlerin darbe ön hasarı sonrası üç nokta eğilme mukavemetlerindeki değişim araştırılmıştır. Darbe enerjisi olarak 5 ve 10 J kullanılmıştır. Bütün numunelerde artan darbe enerjisinin numune mukavemetini düşürdüğü görülmüştür. Darbeden en çok etkilenen modelin cam fiber yüzey malzemesine sahip numuneler olduğu tespit edilmiştir.Öğe Yapıştırıcı ve perçinle birleştirilmiş çift bindirme bağlantılarında ilerlemeli hasar analizi(Fırat Üniversitesi, 2011) Topkaya, Tolga; Solmaz, Murat YavuzBu çalışmada, yapıştırıcı ve perçin kullanılarak birleştirilmiş çift bindirme bağlantılarında ilerlemeli hasar analizi gerçekleştirilmiştir. Bağlantılarda ana malzeme olarak örgü tipi cam fiber takviyeli kompozit malzeme kullanılmıştır. Analizler APDL (Parametric Design Language) kodlan kullanılarak yazılan bir program yardımı ile Ah/SYS 12.1 sonlu elamanlar paket programı kullanılarak gerçekleştirilmiştir. 30, 45 ve 60 mm olmak üzere üç farklı bindirme mesafesi için yapıştırıcı ve perçin kullanılarak birleştirilmiş bağlantıların ilerlemeli hasar analizi sonucunda elde edilen hasar yükleri ve hasar tipleri Maksimum Kayma Gerilmesi Teorisi ve Hashin Kriterine göre tespit edilmiştir. Elde edilen sonuçlar birleştirme tipine ve bindirme mesafesine göre karşılaştırılarak sunulmuştur.Öğe Finite element analysis of the stress distributions in peri-implant bone in modified and standard-threaded dental implants(Taylor & Francis, 2016-01) Topkaya, Tolga; Dündar, Serkan; Solmaz, Murat Yavuz; Yaman, Ferhan; Atalay, Yusuf; Saybak, Arif; Asutay, Fatih; Çakmak, ÖmerThe aim of this study was to examine the stress distributions with three different loads in two different geometric and threaded types of dental implants by finite element analysis. For this purpose, two different implant models, Nobel Replace and Nobel Active (Nobel Biocare, Zurich, Switzerland), which are currently used in clinical cases, were constructed by using ANSYS Workbench 12.1. The stress distributions on components of the implant system under three different static loadings were analysed for the two models. The maximum stress values that occurred in all components were observed in FIII (300 N). The maximum stress values occurred in FIII (300 N) when the Nobel Replace implant is used, whereas the lowest ones, in the case of FI (150 N) loading in the Nobel Active implant. In all models, the maximum tensions were observed to be in the neck region of the implants. Increasing the connection between the implant and the bone surface may allow more uniform distribution of the forces of the dental implant and may protect the bone around the implant. Thus, the implant could remain in the mouth for longer periods. Variable-thread tapered implants can increase the implant and bone contact.Öğe Havacılık ve uzay yapılarında kullanılan bal peteği sandviç kompozitlerin darbe davranışlarının deneysel ve sayısal araştırılması(Batman Üniversitesi, 2018) Topkaya, Tolga; Solmaz, Murat YavuzÖğe Progressive failure analysis in adhesively, riveted, and hybrid bonded double-lap joints(Taylor & Francis, 2013-11) Topkaya, Tolga; Solmaz, Murat YavuzOne of the important processes in structural design is the joining technique. Failure of composite joints involves different failure mechanisms depending upon the joining technique. In this study, a progressive failure analysis was performed on adhesively, riveted, and hybrid bonded double-lap joints. In the joints, a woven-type fiberglass-reinforced composite material was used as the main material; AV 2015 was used as the adhesive, and steel as the rivet material. The analyses were performed using ANSYS 12.1 finite element package software via software written using parametric design language (APDL) codes. At the end of the progressive failure analysis, failure loads and failure modes were determined for 30-, 45-, and 60-mm overlap lengths in accordance with the Maximum Shear Stress Theory and Hashin Criteria. For 45-mm overlap lengths, the joint strength of hybrid joints proved to be 2.72 and 1.145 times higher, respectively, than adhesive and fastening joints. Results showed that the failure load of the joint increased when the overlap length increased. In riveted joints, the failure occurring in the composite plates began around the rivet hole and the catastrophic failure of these types of joints resulted from fiber tensile failure.Öğe Grafen nanopartikül takviyeli epoksi kompozitlerin aşınma davranışı(Dicle Üniversitesi, 2018-11) Çelik, Yahya Hışman; Topkaya, TolgaNanoboyutlu dolgu maddeleri, nanotakviyeli kompozitlerin mekanik, termal ve elektriksel özelliklerini iyileştirir. Mevcut çalışmada grafen (G) nanopartikül takviyeli epoksi kompozitlerin aşınma davranışı pin on disk cihazı kullanılarak araştırılmıştır. Bu doğrultuda, takviyesiz epoksi ile %0.1, %0.2, %0.3, %0.4 ve %0.5 oranında G nanopartikül içeren epoksi kompozitler üretilmiştir. Üretilen kompozitlerin adhesiv aşınma deneyleri gerçekleştirilmiştir. Adhesiv aşınma deneylerinde, yük, kayma hızı ve kayma mesafesi sırasıyla 10 N, 0.35 m/s ve 250 m seçilmiştir. Ayrıca aşındırıcı olarak 5 mm çapa sahip paslanmaz çelik bilye kullanılmıştır. Sonuçlar artan takviye oranının numunelerin aşınma mukavemetini arttırdığını göstermiştir. Nanoboyutlu dolgu maddeleri, nanotakviyeli kompozitlerin mekanik, termal ve elektriksel özelliklerini iyileştirir. Mevcut çalışmada grafen (G) nanopartikül takviyeli epoksi kompozitlerin aşınma davranışı pin on disk cihazı kullanılarak araştırılmıştır. Bu doğrultuda, takviyesiz epoksi ile %0.1, %0.2, %0.3, %0.4 ve %0.5 oranında G nanopartikül içeren epoksi kompozitler üretilmiştir. Üretilen kompozitlerin adhesiv aşınma deneyleri gerçekleştirilmiştir. Adhesiv aşınma deneylerinde, yük, kayma hızı ve kayma mesafesi sırasıyla 10 N, 0.35 m/s ve 250 m seçilmiştir. Ayrıca aşındırıcı olarak 5 mm çapa sahip paslanmaz çelik bilye kullanılmıştır. Sonuçlar artan takviye oranının numunelerin aşınma mukavemetini arttırdığını göstermiştir.Öğe Mechanical properties of fiber/graphene epoxy hybrid composites(SpringerLink, 2020-11-18) Çelik, Yahya Hışman; Topkaya, Tolga; Kılıçkap, ErolThe aim of this study is to determine the effect of graphene nanoparticle (GNP) reinforcement on the mechanical properties of glass fiber reinforced polymer (GFRP), carbon fiber reinforced polymer (CFRP) and aramid fiber reinforced polymer (AFRP) composites commonly used in the space and defense industry. Accordingly, GFRP, CFRP and AFRP composites were produced by using hot pressing method. In addition, hybrid fiber composites were produced by adding 0.1 %, 0.2 % and 0.3 % GNP to these fiber reinforced composites. The tensile strength and modulus of elasticity of the composites were determined. The tensile damage fracture regions were analyzed by scanning electron microscopy (SEM) and energy distribution spectrum (EDS). It was observed that the addition of 0.2 wt. % GNP to GFRP and CFRP composites increased tensile strength and modulus of elasticity. However, the addition of 0.2 wt. % GNP to AFRP composites had no effect on the tensile strength; on the contrary, it partially reduced the tensile strength but increased the modulus of elasticity. On the fracture damage surfaces of the GFRP and CFRP composites and the GNP/GFRP and GNP/CFRP hybrid composites, the fibers were completely separated. On the damage surfaces of AFRP composite and GNP/AFRP hybrid composites, the fibers were deformed but these fibers were not separated from each other. From the EDS analysis, it was observed that the element C increased in the composites with the addition of GNP to the fiber reinforced compositesÖğe Numerical analysis of the effect of implant geometry to stress distributions of dental implant system(University of Utah, 2013-04) Adin, Hamit; Topkaya, Tolga; Solmaz, Murat Yavuz; Dündar, SerkanIn accordance with the increase in their success rate, dental implants have become a popular treatment option for missing teeth. In long-term clinical application, the survival rate for dental implants is over 90% [1,2]. In general, the success of dental implants is related to the quality and quantity of local bones, implant design and surgical technique. Implant diameter and length are accepted as key factors [3,4]. Present work focuses to investigate the effect of titanium implant geometry to stress distributions around mandible and implant system. For this purpose three different implant models which are currently being used in clinical cases constructed by using ANSYS Workbench 12.1. The stress distributions on components of implant system and mandible under static loading were analyzed for all models
- «
- 1 (current)
- 2
- 3
- »