5 sonuçlar
Arama Sonuçları
Listeleniyor 1 - 5 / 5
Öğe N-type InP Schottky diodes with organic thin layer: Electrical and interfacial properties(Journal of Vacuum Science & Technology B, 2010-03) Güllü, Ömer; Turut, AbdulmecitThe rectifying junction characteristics of methyl red (MR) organic film on n-type InP substrate have been studied. It has been observed that MR-based structure shows an excellent rectifying behavior and that the MR film increases the effective barrier height by influencing the space charge region of the n-type InP. The barrier height and ideality factor values for this structure have been obtained as 0.75 eV and 1.93 from the forward bias current-voltage characteristics, respectively. By using capacitance-voltage characteristics at 1 MHz, the barrier height and the carrier concentration values have been calculated as 0.93 eV and 5.13×1015 cm−3, respectively. The energy distributions of the interface states and their relaxation times have been determined from the forward bias capacitance-frequency and conductance-frequency characteristics. Moreover, it was seen that both the interface-state density and the relaxation time of the interface states decreased with bias voltage from experimental results.Öğe Control of barrier heigth ofmetal/semiconductor contacts bymolecular organic film(2011-06) Güllü, Ömer; Turut, Abdulmecit; Kılıçoğlu, Tahsin; Özerden, EniseÖğe Electrical characteristics of the Al/Congo Red (CR)/p-Si semiconductor diodes(Dumlupınar Üniversitesi, 2015-05) Güllü, Ömer; Pakma, Osman; Turut, Abdulmecit; Arsel, İsmailIn this work, we have studied the electrical characteristics of the Al/CR/p-Si MIS Schottky structures formed by coating of the organic material directly on p-Si substrate. It has been seen that the CR thin film on the p-Si substrate has indicated a good rectifying behavior. The barrier height and the ideality factor of the device have been calculated from the I-V characteristic. We have also studied the suitability and possibility of the MIS diodes for use in barrier modification of Si MS diodes. In addition, we have compared the parameters of the Al/CR/p-Si MIS Schottky diodes with those of conventional Al/p-Si MS diodes. We have observed that the b value of 0.77 eV obtained for the Al/CR/p-Si device was significantly larger than BH value of the conventional Al/p-Si MS contact. Thus, the modification of the interfacial potential barrier for metal/Si diodes has been achieved by using the CR organic interlayer. This was attributed to the fact that the CR interlayer increased the effective b by influencing the space charge region of Si. The interface-state density of the MIS diode was found to vary from 1.24×1013 eV-1 cm-2 to 2.44×1012 eV-1 cm-2.Öğe Electrical properties of safranine T p Si organic inorganic semiconductor devices(Cambridge University, 2010-04-25) Güllü, Ömer; Asubay, Sezai; Biber, Mehmet; Kılıçoğlu, Tahsin; Turut, AbdulmecitWe investigated the current-voltage (I-V) and capacitance-voltage (C-V) characteristics of identically prepared safranine T/p-Si organic/inorganic Schottky devices (total 26 diodes) formed by evaporation of organic compound solution on p-Si semiconductor substrate. It was seen that the safranine T organic thin film on the p-Si substrate showed a good rectifying behavior. The barrier heights and ideality factors of all devices were extracted from the electrical characteristics. The mean barrier height and mean ideality factor from I-V measurements were calculated as 0.59±0.02 eV and 1.80±0.20, respectively. Also, the mean barrier height and mean acceptor doping concentration from C-V measurements were calculated as 0.67±0.10 eV and (6.96±0.37)×1014 cm-3, respectively. The discrepancy in the barrier height values obtained from I-V and C-V characteristics has been attributed to different nature of the measurements. The discrepancy between these values can also be due to the existence of the interfacial native oxide and the organic safranine T thin layer between the semiconductor substrate and top contact metal.Öğe Current-voltage, capacitance-voltage-frequency and ınterface characteristics ofmetal/organic dye molecule/P-Type Inp photovoltaic device(2011-09) Güllü, Ömer; Özerden, Enise; Kılıçoğlu, Tahsin; Turut, Abdulmecit
