    Experimental determination of the static and fatigue strength of theadhesive joints bonded by epoxy adhesive including different particles
    (Elsevier, 2018-12) Adin, Hamit; Saraç, İsmail; Temiz, Şemsettin
    Because of their many advantages, adhesively bonded joints are intensively used in many engineeringfields. So,the mechanical research of the adhesively bonded joints is very important to use these joints safely. There aremany studies performed by researchers to investigate the mechanical properties of the adhesive joints. There hasbeen a considerable interest in nanoparticles added to structural adhesives recently because nanoparticles im-prove the mechanical properties of adhesives and joints. In this paper, different nanoparticles reinforced byepoxy adhesive, and neat adhesive were used to produce single lap joints. The static and fatigue strengths ofsingle lap joints incorporating nanoparticles were compared to those without nanoparticles. Experiments wereperformed at 20 mm overlap length. DP460 epoxy was used as the adhesive material, and nano-Al2O3, nano-TiO2and nano-SiO2were used as the nanoparticles; and AISI 304 stainless steel plates were used as the adherents. Theresults of the experimental research revealed that average failure load increased significantly in nanoparticle-reinforced adhesive joints. The highest average failure load was obtained with 4 wt% nano-Al2O3in epoxyadhesive. Fatigue tests were performed at 10 Hz frequency, and 0.1 loading ratio (R). When the fatigue testresults were examined, it was observed that the addition of the nano-Al2O3and nano-SiO2to the adhesiveincreased fatigue strength of the adhesive joints, on the other hand, the addition of the nano-TiO2to the adhesivereduced fatigue strength of the adhesive joints.
  • Küçük Resim
    Öğe
    Experimental determination of the mechanical properties of adhesive joints bonded epoxy adhesive included Al2O3 nanoparticule
    (European Journal of Technic, 2016-08-01) Adin, Hamit; Saraç, İsmail; Temiz, Şemsettin
    Yapıştırma bağlantılarında, yapıştırıcı içerisine katılan nanopartiküllerin, bağlantıların mekanik özelliklerine etkisi ile ilgili araştırmalar son zamanlarda dikkat çekmektedir. Bu çalışmada; epoksi yapıştırıcı içerisine % 2 oranında Al2O3 nanopartikül katılarak ve katkısız epoksi yapıştırıcı kullanılarak tek tesirli bindirme bağlantıları oluşturulmuş ve bağlantıların mekanik özellikleri çekme yükü altında 20 mm, 25 mm ve 30 mm bindirme boylarında deneysel olarak incelenmiştir. Deneysel çalışmalarda DP460 epoksi yapıştırıcısı, Al2O3 nanopartikülleri ve yapıştırılan malzeme olarak St-37 çeliği kullanılmıştır. Deneylerden elde edilen sonuçlar incelendiğinde; % 2 Al2O3 nanopartikül katkılı yapıştırıcıların kullanılmasıyla 20 mm ve 30 mm bindirme boylu bağlantılarda genel olarak hasar yükü azalmıştır. Ancak 25 mm bindirme boyunda % 5 oranında bir artış görülmüştür. Ayrıca nanopartikül ilavesi bağlantıların uzama kapasitelerine azaltıcı yönde etki yapmıştır.