    Investigation of mechanical characteristics of GFRP composites produced from chopped glass fber and application of taguchi methods to turning operations
    (SpringerLink, 2020-04-08) Çelik, Yahya Hışman; Türkan, Cihat
    Glass fber-reinforced plastic (GFRP) composites take place in engineering materials owing to their low-weight and high-mechanical properties. In some cases, they need to be shaped by machining before using in industrial applications. However, when these composites are machined, many problems such as bad surface quality, rapid tool wear are encountered. Therefore, optimization of cutting parameters is essential to eliminate or minimize these problems. In this study, GFRP composites were produced by combining polyester matrix material with glass fbers (GF) having 6 mm, 6–12 mm, 12 mm fber length, and 20%, 25%, 30% fber ratio by weight. The tensile strengths of these composites were investigated. Turning tests were also performed with cutting speeds of 40, 80, and 120 m/min, feed rates of 0.1, 0.2 and 0.3 mm/rev, and depth of cut of 1, 2, and 3 mm, according to Taguchi L27 standard orthogonal array method. The efect of fber length and ratio, and cutting parameters on cutting forces and surface roughness were analyzed. As a result of the experiments, it was observed that the reinforced polymer matrix with GF provide to increase the tensile strength. The highest tensile strength was obtained as 55.95 MPa from the composite having a fber length of 12 mm and a fber ratio of 25%. Besides, the feed rate was determined as the most efective parameter among the all parameters on both cutting force and surface roughness. Therefore, the feed rate should be chosen low for lower cutting force and surface roughness values.
  • Küçük Resim Yok
    Öğe
    Environmental effects on mechanical properties of glass-epoxy composites
    (De Gruyter, 2014-05) Deniz, Mehmet Emin; Karakuzu, Ramazan; Kanlıoğlu, Halit
    This study presents the effects of seawater and distilled water immersion time periods on mechanical properties of unidirectional glass reinforced epoxy composites. Tension, compression, and shear test specimens exposed to seawater and distilled water were prepared according to ASTM standards. After tests, SEM imaging of fracture surface of specimens was made. Results showed that seawater and distilled water immersion time affects significantly mechanical properties and strength values of glass-epoxy composites.
  • Küçük Resim
    Öğe
    Şanlıurfa-Hacı Yadigâr Camii restorasyon amaçlı yapı malzemelerinin arkeometrik özelliklerinin incelenmesi
    (Türkiye Bilimler Akademisi, 2019-06-15) Aydın, Mahmut; Tetiker, Sema; Tanrıkulu, Hüseyin
    Hacı Yadigar Camii Şanlıurfa il merkezi’nde bulunmakta ve ilin en eski camilerinden biridir. Hacı Yadigar Camii, iç kapısı üzerindeki kitabedeki açıklamalarda yapının 1155 (hicri 550) ve 1514 (hicri 920) yıllarında restorasyonu yapıldı yazmaktadır. Şair Sabır tarafından yazılan kitabede ise son restorasyon tarihi 1871 (hicri 1288) olarak verilmiştir. Hacı Yadigar Camisi’nin 2018 tarihinde yapılması planlanan restorasyon projesinin hazırlanması aşamasında yapı malzemelerinin arkeometrik özelliklerinin tanımlanması amacıyla tahribatsız ve tahribatlı yöntemlerle analizler yapılmıştır. Yapıdan örnekler alınmış olup, bu örnekler üzerinde optik petrografi (polarizan mikroskop), X-ışınları difraksiyonu (XRD) ve jeokimyasal analizler (X-ışınları flöresans-XRF) yapılmıştır. Bu kapsamda caminin farklı bölümlerindeki yapı malzemelerini temsil eden 12 adet harç ve taş malzeme örnekleri toplanmıştır. Optik petrografik incelemelere göre kireçtaşları bütünüyle kalsit minerallerinden az miktarda ise kuvars, feldispat, kil, opak mineral, fosil kavkısı ve maserallerle temsil edilmektedir. XRD-Tüm kayaç (XRD-TK) inceleme sonuçlarına göre örneklerde kalsit, jips, kuvars, feldispat ve kil mineralleri saptanmıştır. Kireçtaşı olarak tanımlanmış olan yapı duvarları kalsit+jips bileşimi gösterirken, harç örneklerinde kalsit+kuvars±feldispat bileşenleri bulunmuştur. P-XRF sonuçlarına göre major elementler (Mg, Al, Si, K, Ca, Fe) ve metal olmayan (S) elementler tespit edilmiştir. Arkeometrik özelikleri belirlenen harç malzemelerinde restorasyonda 5-7% oranında tuğla kırığı ve/veya kum içeren kireç harçlarının, yapıtaşlarında ise uygun maseral (fusinit) içeren ilksel yapıtaşına uygun jeolojik formasyonun saptanarak bu yapıtaşlarının kullanılması önerilmektedir.