  • Öğe
    Improvement of diode parameters in Al/n-Si schottky diodes with coronene interlayer using variation of the illumination intensity
    (Elsevier, 2017-12-15) Pakma, Osman; Çavdar, Şükrü; Koralay, Haluk; Tuğluoğlu, Nihat; Yüksel, Ömer Faruk
    In present work, Coronene thin films on Si wafer have been deposited by the spin coating method. It has been ultimately produced Al/Coronene/n-Si/In Schottky diode. Current–voltage (I-V) measurements have been used to determine the effect of illumination intensity in the Schottky diodes. The barrier height (ΦB) values increased as ideality factor (n) values decreased with a increase in illumination intensity. The ΦB values have been found to be 0.697 and 0.755 eV at dark and 100 mW/cm2, respectively. The n values have been found to be 2.81 and 2.07 at dark and 100 mW/cm2, respectively. Additionally, the series resistance (Rs) values from modified Norde method and interface state density (Nss) values using current-voltage measurements have been determined. The values of Rs have been found to be 1924 and 5094 Ω at dark and 100 mW/cm2, respectively. The values of Nss have been found to be 4.76 × 1012 and 3.15 × 1012 eV−1 cm−2 at dark and 100 mW/cm2, respectively. The diode parameters are improved by applying the variation of illumination intensity to the formed Schottky diodes.
  • Öğe
    High barrier Schottky diode with organic interlayer
    (Elsevier, 2012-03) Güllü, Ömer; Aydoğan, Şakir; Türüt, Abdülmecit
    A new Cu/n-InP Schottky junction with organic dye (PSP) interlayer has been formed by using a solution cast process. An effective barrier height as high as 0.82 eV has been achieved for Cu/PSP/n-InP Schottky diodes, which have good currentvoltage (IV) characteristics. This good performance is attributed to the effect of formation of interfacial organic thin layer between Cu and n-InP. By using capacitancevoltage measurement of the Cu/PSP/n-InP Schottky diode the diffusion potential and the barrier height have been calculated as 0.73 V and 0.86 eV, respectively. From the IV measurement of the diode under illumination, short circuit current (I sc) and open circuit voltage (V oc) have been extracted as 0.33 μA and 150 mV, respectively.